Glass resistance to radiation-part I: Preliminary investigation of three commercial glass fibers | |
Zu, Qun1; Song, Wei1; Zeng, Huidan2; Yu, Xiaowu3; Huang, Songlin1; Huang, Sanxi1; Li, Hong4 | |
2020-05-26 | |
发表期刊 | INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE |
ISSN | 2041-1286 |
通讯作者 | Zu, Qun(zuqun@fiberglasschina.com) |
摘要 | The effects of gamma-radiation on properties of three types of commercial alkaline earth aluminosilicate glasses (NJE, NJ1, NJ2) were investigated at 5M Gy dosage, using samples of bulk glass, glass fiber, and fiber reinforced laminate epoxy composite. The radiation-induced defect generation and structural modifications in the bulk glasses were characterized by UV-VIS-NIR, FTIR absorption spectroscopy, respectively. Strong radiation resistance was found in NJ2 composed of high content of glass former such as Si and Al, together with variable Fe and Ce oxide. Mechanical properties of the fiber woven fabric taps and reinforced laminate composites were investigated before and after the irradiation. While the tap samples showed minor property degradations after the irradiation, all composite samples degraded by greater than 19% in tensile strength and greater than 55% in interlaminate shear strength (ILSS) at 5M Gy dose level. Deterioration of the composite mechanical properties is primarily attributed to the radiation damage to the epoxy resin and in turn, the failure mode of the irradiated composite samples is dominated by delamination at the interfaces between the fiber glass tapes and the resin under the applied tensile load or shear as compared with the failure mode of fiber breakages for their counterparts without gamma-irradiation. |
关键词 | glass fiber glass reinforced plastic composites glass structure mechanical property gamma-radiation |
DOI | 10.1111/ijag.15612 |
关键词[WOS] | TEMPERATURE FAST-NEUTRON ; GAMMA-IRRADIATION ; EPOXY COMPOSITE ; BORATE GLASSES ; OXIDE GLASSES ; FUSION ; ITER ; RAMAN ; SPECTROSCOPY ; BEHAVIOR |
收录类别 | SCI |
语种 | 英语 |
资助项目 | National Key Laboratory for Special Fiber composites ; project of Material Application and Validation |
项目资助者 | National Key Laboratory for Special Fiber composites ; project of Material Application and Validation |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Ceramics |
WOS记录号 | WOS:000535267800001 |
出版者 | WILEY PERIODICALS, INC |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/103178 |
专题 | 中国科学院合肥物质科学研究院 |
通讯作者 | Zu, Qun |
作者单位 | 1.Sinoma Sci & Technol Co Ltd, Nanjing Glass Fiber Res & Design Inst, Nanjing, Peoples R China 2.East China Univ Sci & Technol, Shanghai, Peoples R China 3.Chinese Acad Sci, Inst Plasma Phys, Hefei, Peoples R China 4.Nippon Elect Glass, Shelby, NC USA |
推荐引用方式 GB/T 7714 | Zu, Qun,Song, Wei,Zeng, Huidan,et al. Glass resistance to radiation-part I: Preliminary investigation of three commercial glass fibers[J]. INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,2020. |
APA | Zu, Qun.,Song, Wei.,Zeng, Huidan.,Yu, Xiaowu.,Huang, Songlin.,...&Li, Hong.(2020).Glass resistance to radiation-part I: Preliminary investigation of three commercial glass fibers.INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE. |
MLA | Zu, Qun,et al."Glass resistance to radiation-part I: Preliminary investigation of three commercial glass fibers".INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE (2020). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论