Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma | |
Zhang,Xue-Xi1,2; Qiao,Li2; Zhang,Hong2; Li,Yu-Hong1; Wang,Peng2![]() | |
2021-03-17 | |
发表期刊 | Nuclear Fusion
![]() |
ISSN | 0029-5515 |
通讯作者 | Li,Yu-Hong() ; Wang,Peng() |
摘要 | AbstractSurface blistering and deuterium (D) retention behaviors in pure tungsten (W) and 0.5 wt% ZrC-doped W alloy (WZC) exposed to D plasma have been investigated as a function of incident D fluence up to 2.6 × 1025?D?m?2. Surface observations show that large-sized blisters (~8–10 μm) and a few small blisters (<2 μm) are formed on the W samples. For WZC, the surface of the samples is covered by a high density of small blisters (<1 μm), and no blister larger than 2 μm is found. Cross section views show that the large-sized blisters originate from subsurface grain boundaries, and the small blisters originate from intra-granular cavities at depths much closer to the surface. The intra-granular blisters are preferentially formed on the grains with a normal direction close to [111] for both types of sample. The inter-granular blisters formed in pure W are significantly suppressed in WZC, and the fluence threshold for blister formation in WZC is lower than that in W. The D depth distributions indicate that the implanted D is mainly retained in the near-surface region of WZC and W. Besides, a higher and broader D peak is observed at a depth of between 0.1–0.25 μm in WZC, but the intensity and width of the D peak is lower and thinner in W. The desorption spectra of WZC shift to the lower temperature side as compared to W, and the total retained D amount in WZC and W is comparable in the fluence range of 2.8 × 1024–2.6 × 1025?D?m?2. |
关键词 | W W-ZrC alloy D plasma surface blistering D retention |
DOI | 10.1088/1741-4326/abdfda |
收录类别 | SCI |
语种 | 英语 |
资助项目 | National key R&D project of China[2017YFE0302500] ; National Natural Science Foundation of China[11875305] ; National Natural Science Foundation of China[11735015] ; National Natural Science Foundation of China[11775102] |
项目资助者 | National key R&D project of China ; National Natural Science Foundation of China |
WOS研究方向 | Physics |
WOS类目 | Physics, Fluids & Plasmas |
WOS记录号 | IOP:0029-5515-61-4-abdfda |
出版者 | IOP Publishing |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/120703 |
专题 | 中国科学院合肥物质科学研究院 |
通讯作者 | Li,Yu-Hong; Wang,Peng |
作者单位 | 1.School of Nuclear Science and Technology, Lanzhou University, Lanzhou 730000, China 2.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, China 3.Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031, China |
推荐引用方式 GB/T 7714 | Zhang,Xue-Xi,Qiao,Li,Zhang,Hong,et al. Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma[J]. Nuclear Fusion,2021,61. |
APA | Zhang,Xue-Xi,Qiao,Li,Zhang,Hong,Li,Yu-Hong,Wang,Peng,&Liu,Chang-Song.(2021).Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma.Nuclear Fusion,61. |
MLA | Zhang,Xue-Xi,et al."Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma".Nuclear Fusion 61(2021). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论