Influence of interactions between alumina crucible and Si-Ca-Fe melt on B and P removal from silicon | |
Sakiani, Hassan1; Tabaian, Seyed Hadi1; Chen, Jian2 | |
2021-01-15 | |
发表期刊 | SEPARATION AND PURIFICATION TECHNOLOGY |
ISSN | 1383-5866 |
通讯作者 | Tabaian, Seyed Hadi(tabaian@aut.ac.ir) |
摘要 | The effect of alumina crucible on different aspects of the solvent refining of silicon by the Si-Ca-Fe system was investigated in this paper. Ca and Fe were added to Si in a wide range of concentrations (0-20 wt%), and the melt composition change resulting from melt-alumina interactions was studied thermodynamically and experimentally. The ratio of Ca concentration in the final melt to its value in the initial mixture was in the range of 0.17-0.23. On the other hand, a considerable amount of Al was identified in the melt together with CaAl4O7, Ca2Al2SiO7, and CaAl2O4 phases as oxide interaction products. A conceptual mechanism was proposed for the evolution of these products. Then, the segregation behavior of impurities during solidification was studied based on Fe or Ca increment in the system, and B and P removal rates were calculated in particular. The higher the Ca or Fe content were, the higher removal rates were achieved. They were also enhanced by cooling the samples in the furnace rather than quenching from 1493 K (1220 degrees C). The directional solidification method was also examined, and it showed the best overall removal rate with 94.9% for P and 63% for B, while its impact on B reduction was more than P. |
关键词 | Silicon purification Solvent refining Alumina Acid leaching Calcium Melt-crucible interaction |
DOI | 10.1016/j.seppur.2020.117743 |
收录类别 | SCI |
语种 | 英语 |
资助项目 | Iran National Science Foundation (INSF)[96001489] ; Niroo Research Institute (NRI)[96/30813/06] ; National Natural Science Foundation of China[51874272] ; National Natural Science Foundation of China[51804294] |
项目资助者 | Iran National Science Foundation (INSF) ; Niroo Research Institute (NRI) ; National Natural Science Foundation of China |
WOS研究方向 | Engineering |
WOS类目 | Engineering, Chemical |
WOS记录号 | WOS:000631006200001 |
出版者 | ELSEVIER |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/120860 |
专题 | 中国科学院合肥物质科学研究院 |
通讯作者 | Tabaian, Seyed Hadi |
作者单位 | 1.Amirkabir Univ Technol, Tehran Polytech, Dept Mat & Met Engn, Tehran 1591634311, Iran 2.Chinese Acad Sci, Hefei Inst Phys Sci, Inst Solid State Phys, Key Lab Photovolta & Energy Conservat Mat, Hefei 230031, Peoples R China |
推荐引用方式 GB/T 7714 | Sakiani, Hassan,Tabaian, Seyed Hadi,Chen, Jian. Influence of interactions between alumina crucible and Si-Ca-Fe melt on B and P removal from silicon[J]. SEPARATION AND PURIFICATION TECHNOLOGY,2021,255. |
APA | Sakiani, Hassan,Tabaian, Seyed Hadi,&Chen, Jian.(2021).Influence of interactions between alumina crucible and Si-Ca-Fe melt on B and P removal from silicon.SEPARATION AND PURIFICATION TECHNOLOGY,255. |
MLA | Sakiani, Hassan,et al."Influence of interactions between alumina crucible and Si-Ca-Fe melt on B and P removal from silicon".SEPARATION AND PURIFICATION TECHNOLOGY 255(2021). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论