Cracking and exfoliation behavior of oxide scale on T91 steel under different tensile stresses in oxygen-controlled lead-bismuth eutectic at 550 degrees C

doi:10.1016/j.corsci.2021.109324

HFCAS OpenIR

	Cracking and exfoliation behavior of oxide scale on T91 steel under different tensile stresses in oxygen-controlled lead-bismuth eutectic at 550 degrees C
	Luo, Lin; Jiang, Zhizhong; Xiao, Zunqi; Huang, Qunying
	2021-05-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
通讯作者	Jiang, Zhizhong(zhizhong.jiang@inest.cas.cn) ; Xiao, Zunqi(zunqi.xiao@inest.cas.cn)
摘要	The effect of different tensile stresses (0-180 MPa) on cracking and exfoliation behavior of oxide scale for T91 steel was studied in lead-bismuth eutectic containing 10-6 wt% oxygen concentration at 550 ?C. The results demonstrate that the exfoliation area of magnetite increased with stress. When tensile stress reached about 180 MPa, only a little magnetite remained; the outer sub-layer of spinel began to crack and locally exfoliated, exposing the inner sub-layer of spinel. The cracks with four different morphologies originated at the outer sublayer of spinel and propagated inward. A model was proposed to explain these phenomena.
关键词	Stress corrosion Lead-bismuth eutectic Oxide scale Cracking Exfoliation
DOI	10.1016/j.corsci.2021.109324
收录类别	SCI
语种	英语
资助项目	National Key R&D Program of China[2018YFE0122100] ; National Natural Science Foundation of China[51501185] ; National Natural Science Foundation of China[51401204] ; National Natural Science Foundation of China[51901224]
项目资助者	National Key R&D Program of China ; National Natural Science Foundation of China
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000632197200001
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：19[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.hfcas.ac.cn:8080/handle/334002/120977
专题	中国科学院合肥物质科学研究院
通讯作者	Jiang, Zhizhong; Xiao, Zunqi
作者单位	Chinese Acad Sci, Hefei Inst Phys Sci, Inst Nucl Energy Safety Technol, Hefei 230031, Anhui, Peoples R China
推荐引用方式 GB/T 7714	Luo, Lin,Jiang, Zhizhong,Xiao, Zunqi,et al. Cracking and exfoliation behavior of oxide scale on T91 steel under different tensile stresses in oxygen-controlled lead-bismuth eutectic at 550 degrees C[J]. CORROSION SCIENCE,2021,183.
APA	Luo, Lin,Jiang, Zhizhong,Xiao, Zunqi,&Huang, Qunying.(2021).Cracking and exfoliation behavior of oxide scale on T91 steel under different tensile stresses in oxygen-controlled lead-bismuth eutectic at 550 degrees C.CORROSION SCIENCE,183.
MLA	Luo, Lin,et al."Cracking and exfoliation behavior of oxide scale on T91 steel under different tensile stresses in oxygen-controlled lead-bismuth eutectic at 550 degrees C".CORROSION SCIENCE 183(2021).