W-10%TiC复合材料的制备与力学性能研究

	W-10%TiC复合材料的制备与力学性能研究
其他题名	Study on Preparation and Mechanical Properties of W-10%TiC Composites
	于福文; 吴玉程; 陈勇; 邓景泉; 陈俊凌
	2008
发表期刊	稀有金属
ISSN	0258-7076
摘要	采用高能球磨手段制备了W-10%TiC（质量分数,下同）纳米复合粉体,并采用热压方法烧结成致密块体,研究了高能球磨、烧结温度、烧结时间及烧结压力对复合材料致密度和力学性能的影响。结果表明：高能球磨后,复合粉体的颗粒形状近似球形,粒径均匀,平均粒径为100nm,并且纳米复合粉体的烧结温度大大降低,其原因是粉体的颗粒细小、扩散系数高、表面能高等性质及球磨过程中少量Fe,Ni杂质的引入。对所制备纳米粉体而言,较合适的烧结工艺为：1700℃,30MPa压力下烧结60min,在此工艺条件下制备的复合材料的致密度达到98.4%,抗弯强度和断裂韧性分别达到：681MPa,6.24MPa·m^1/2。
合作性质	其它
其他摘要	W-10%TiC composites were prepared by high energy ball milling and vacuum hot-pressing （VHP） and sintering. The effects of high energy milling, sintering temperature, holding time and hot pressure on the composites were investigated. The results show that the nanocomposite powders with homogeneous particle size about 100 nm were obtained through high energy milling processing. The nanocomposite powders were consolidated to bulk with high density at low temperature, which was caused by the fine particles having high diffusion coefficient, high surface energy and the impurity of Fe, Ni introduced from the process of high energy milling. The relative density, flexural strength and fracture toughness of the composites prepared under the optimal condition 1700 ℃, 30 MPa for 60 min could reach to 98.6%, 681 MPa and 6.24 MPa·m^1/2, respectively.
关键词	高能球磨热压 W-TiC 致密度力学性能
学科领域	新能源材料与工程
收录类别	其他
语种	中文
CSCD记录号	CSCD:3246705
文献类型	期刊论文
条目标识符	http://ir.hfcas.ac.cn:8080/handle/334002/1214
专题	中科院等离子体物理研究所
推荐引用方式 GB/T 7714	于福文,吴玉程,陈勇,等. W-10%TiC复合材料的制备与力学性能研究[J]. 稀有金属,2008,032(2).
APA	于福文,吴玉程,陈勇,邓景泉,&陈俊凌.(2008).W-10%TiC复合材料的制备与力学性能研究.稀有金属,032(2).
MLA	于福文,et al."W-10%TiC复合材料的制备与力学性能研究".稀有金属 032.2(2008).

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
W-10%TiC复合材料的制备与力学性能（236KB）			开放获取	使用许可	浏览下载