Microstructures, Thermal and Mechanical Properties of Pure Tungsten—A Comparison Between Selective Laser Melting and Hot Rolling | |
Wang,Chong1; Chen,Daobing1; Zhou,Yan2; Xie,Zhuoming3![]() ![]() | |
2022-05-04 | |
发表期刊 | Chinese Journal of Mechanical Engineering
![]() |
ISSN | 1000-9345 |
通讯作者 | Zhou,Yan(zhouyan@cug.edu.cn) ; Wen,Shifeng(roya_wen@hust.edu.cn) |
摘要 | AbstractA comparative study on the influence of different manufacturing methods (selective laser melting and hot rolling) on the microstructure, mechanical and thermal behaviours of tungsten (W) was presented for the first time. The results indicated that the selective laser melting (SLM) W exhibited a finer grain sizes, a lower strength ductility, hardness and thermal conductivity compared to hot-rolled W. The main reason for this result was that the laser underwent rapid heating and cooling when it was used to melt W powder with high energy density, resulting in large internal stress in the sample after manufacturing. Subsequently, the internal stress was released, leading to the generation of micro-cracks at the grain boundaries, thereby affecting the performance of SLM W samples. In addition, the higher fraction of high-angle grain boundaries (HAGBs) of SLM W was found to be the key factor for intrinsic brittleness. Because the HAGBs are the preferred crack paths, which could promote crack propagation and decrease fracture energy. |
关键词 | Tungsten (W) Selective laser melting (SLM) Hot rolling Microstructure Thermal conductivity Mechanical property |
DOI | 10.1186/s10033-022-00712-5 |
语种 | 英语 |
WOS记录号 | BMC:10.1186/s10033-022-00712-5 |
出版者 | Springer Nature Singapore |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/128732 |
专题 | 中国科学院合肥物质科学研究院 |
通讯作者 | Zhou,Yan; Wen,Shifeng |
作者单位 | 1.Huazhong University of Science and Technology; State Key Laboratory of Material Processing and Die & Mold Technology, School of Materials Science and Engineering 2.China University of Geosciences; Faculty of Engineering 3.Chinese Academy of Sciences; Key Laboratory of Materials Physics, Institute of Solid State Physics |
推荐引用方式 GB/T 7714 | Wang,Chong,Chen,Daobing,Zhou,Yan,等. Microstructures, Thermal and Mechanical Properties of Pure Tungsten—A Comparison Between Selective Laser Melting and Hot Rolling[J]. Chinese Journal of Mechanical Engineering,2022,35. |
APA | Wang,Chong.,Chen,Daobing.,Zhou,Yan.,Xie,Zhuoming.,Fang,Qianfeng.,...&Yan,Chunze.(2022).Microstructures, Thermal and Mechanical Properties of Pure Tungsten—A Comparison Between Selective Laser Melting and Hot Rolling.Chinese Journal of Mechanical Engineering,35. |
MLA | Wang,Chong,et al."Microstructures, Thermal and Mechanical Properties of Pure Tungsten—A Comparison Between Selective Laser Melting and Hot Rolling".Chinese Journal of Mechanical Engineering 35(2022). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论