Corrosion characteristics of T91 steel in lead–bismuth eutectic with different oxygen concentrations at 500°C | |
Shujian Tian1; Yongqiang Pang1; Zhizhong Jiang2![]() ![]() | |
2021-08-29 | |
发表期刊 | Materials and Corrosion-Werkstoffe und Korrosion
![]() |
DOI | 10.1002/maco.202112505 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/132345 |
专题 | 中国科学院核能安全技术研究所 |
通讯作者 | Zhizhong Jiang |
作者单位 | 1.School of Electric Power, North China University of Water Resources and Electric Power, Zhengzhou, Henan, China 2.Institute of Nuclear Energy Safety Technology, Hefei Institutes of Physical Science, Chinese Academy of Sciences, Hefei, Anhui, China |
推荐引用方式 GB/T 7714 | Shujian Tian,Yongqiang Pang,Zhizhong Jiang,等. Corrosion characteristics of T91 steel in lead–bismuth eutectic with different oxygen concentrations at 500°C[J]. Materials and Corrosion-Werkstoffe und Korrosion,2021. |
APA | Shujian Tian,Yongqiang Pang,Zhizhong Jiang,Lin Luo,&Zunqi Xiao.(2021).Corrosion characteristics of T91 steel in lead–bismuth eutectic with different oxygen concentrations at 500°C.Materials and Corrosion-Werkstoffe und Korrosion. |
MLA | Shujian Tian,et al."Corrosion characteristics of T91 steel in lead–bismuth eutectic with different oxygen concentrations at 500°C".Materials and Corrosion-Werkstoffe und Korrosion (2021). |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论