| 等离子壁材料钨基纳米粉末的制备 | |
| 其他题名 | Preparation of tungsten matrix nanocrystalline powders for plasma facing materials |
于福文; 吴玉程; 陈勇; 陈俊凌
| |
| 2008 | |
| 发表期刊 | 核聚变与等离子体物理
 |
| ISSN | 0254-6086 |
| 摘要 | 用机械合金化的方法制备了可为等离子壁材料的W-30％TiC（体积百分数）纳米复合粉末。用BET N2吸附法测量了球磨前后复合粉末的比表面，用激光粒度仪测量复合粉末的粒径分布，用X射线衍射分析了粉末的晶粒尺寸，用SEM观察了球磨前后粉末形貌。研究结果表明，W-TiC粉末的最佳球磨参数为：球磨介质比约2：1，球料比约10：1，球磨转速约200r·min^-1，球磨时间约25h。 |
| 合作性质 | 其它 |
| 其他摘要 | W-30%TiC nanocrystalline composite powders for plasma facing materials were prepared by mechanical alloying. Influences of parameters of mechanical alloying process such as liquid-to-balls-and-powders ratio, ball-to-powder ratio, milling speed and milling time on characteristics of the milled powders were studied. The optimal mechanical alloying process parameters were the liquid-to-balls-and-powders ratio 2：1, ball-to-powders ratio 10：1, milling speed 200r-min^-1 and milling time 25h, respectively. |
| 关键词 | 机械合金化 钨 碳化钛 纳米复合粉体 |
| 学科领域 | 新能源材料与工程 |
| 收录类别 | 其他 |
| 语种 | 中文 |
| CSCD记录号 | CSCD:3219052 |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/1334 |
| 专题 | 中科院等离子体物理研究所 |
| 推荐引用方式 GB/T 7714 | 于福文,吴玉程,陈勇,等. 等离子壁材料钨基纳米粉末的制备[J]. 核聚变与等离子体物理,2008,028(1). |
| APA | 于福文,吴玉程,陈勇,&陈俊凌.(2008).等离子壁材料钨基纳米粉末的制备.核聚变与等离子体物理,028(1). |
| MLA | 于福文,et al."等离子壁材料钨基纳米粉末的制备".核聚变与等离子体物理 028.1(2008). |
| 条目包含的文件 | 下载所有文件 | |||||
| 文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
| 等离子壁材料钨基纳米粉末的制备.pdf（266KB） | 开放获取 | 使用许可 | 浏览 下载 | |||
| 个性服务 |
| 推荐该条目 |
| 保存到收藏夹 |
| 查看访问统计 |
| 导出为Endnote文件 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| [于福文]的文章 |
| [吴玉程]的文章 |
| [陈勇]的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| [于福文]的文章 |
| [吴玉程]的文章 |
| [陈勇]的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| [于福文]的文章 |
| [吴玉程]的文章 |
| [陈勇]的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论