High-Temperature Phase Relations in the Lu2O3-Ta2O5 System | |
Xing, Xue1,2; Wang, Xiaofei1,2; Zhang, Qingli1,4; Sun, Guihua1; Shi, Chaoshu3; Liu, Wenpeng1; Sun, Dunlu1; Yin, Shaotang1 | |
2016-03-01 | |
发表期刊 | JOURNAL OF THE AMERICAN CERAMIC SOCIETY |
摘要 | The compounds formed from the Lu2O3-Ta2O5 system in the composition range 25-60 mol% Ta2O5 were prepared by solid-state reaction from 1350 degrees C to 2058 degrees C, and the phase transitions were investigated by X-ray diffraction (XRD). Cubic Lu3TaO7, M-LuTaO4, M-LuTaO4, O-Ta2O5, and T-Ta2O5 are observed. With the temperature increase, there is an irreversible phase transition from M to M-LuTaO4 near 1770 degrees C in the composition of 30-52 mol% Ta2O5, and another phase transition from T-Ta2O5 to O-Ta2O5 at about 1685 degrees C when the ratio of Ta2O5 is >52 and 60 mol%. A phase diagram of the Lu2O3-Ta2O5 system in the range 0-100 mol% Ta2O5 was constructed. These results are helpful to explain the phase transition of Lu2O3-Ta2O5 system and design the preparation technique of LuTaO4 single crystal or ceramic scintillator, which may be applied in the fields of nuclear medicine and high-energy physics. |
文章类型 | Article |
WOS标题词 | Science & Technology ; Technology |
DOI | 10.1111/jace.13977 |
关键词[WOS] | X-RAY PHOSPHORS ; LUMINESCENCE ; CRYSTAL ; YB |
收录类别 | SCI |
语种 | 英语 |
项目资助者 | National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; National Natural Science Foundation of China(51 172 236 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 272 254 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 51 102 239 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 205 173 ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) ; 61 405 206) |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Ceramics |
WOS记录号 | WOS:000372189300043 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/21532 |
专题 | 中科院安徽光学精密机械研究所 |
作者单位 | 1.Chinese Acad Sci, Anhui Inst Opt & Fine Mech, Key Lab Photon Devices & Mat Anhui Prov, POB 1125, Hefei 230031, Anhui, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Univ Sci & Technol China, Dept Phys, Hefei 230026, Peoples R China 4.Chinese Acad Sci, Anhui Inst Opt & Fine Mech, POB 1125, Hefei 230031, Anhui, Peoples R China |
第一作者单位 | 中科院安徽光学精密机械研究所 |
推荐引用方式 GB/T 7714 | Xing, Xue,Wang, Xiaofei,Zhang, Qingli,et al. High-Temperature Phase Relations in the Lu2O3-Ta2O5 System[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2016,99(3):1042-1046. |
APA | Xing, Xue.,Wang, Xiaofei.,Zhang, Qingli.,Sun, Guihua.,Shi, Chaoshu.,...&Yin, Shaotang.(2016).High-Temperature Phase Relations in the Lu2O3-Ta2O5 System.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,99(3),1042-1046. |
MLA | Xing, Xue,et al."High-Temperature Phase Relations in the Lu2O3-Ta2O5 System".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 99.3(2016):1042-1046. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
High-Temperature Pha(803KB) | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论