KTN晶体及其熔体结构的高温拉曼光谱研究 | |
其他题名 | High temperature Raman spectra and micro-structure of KTN crystal and melt |
2009-01-01 | |
发表期刊 | 物理学报 |
ISSN | 1000-3290 |
摘要 | 测量并研究了不同温度(室温—1573K)范围内KTN晶体的拉曼光谱及其熔体的高温拉曼光谱,分析了KTN晶体结构随温度变化的规律及其熔体的结构特征.随着温度的升高,KTN晶体的拉曼光谱谱峰都不同程度地向低波数方向移动,同时存在不同程度的展宽,并伴随强度的减弱.观察并解释了温度353K附近KTN晶体样品的四方—立方转相现象.研究了KTN晶体拉曼光谱中538cm-1,585cm-1,835cm-1和877cm-1谱峰及其熔体高温拉曼光谱中868cm-1谱峰的出现、消失、峰强变化等特殊现象.在KTN高温熔体中,Ta/NbO6八面体结构基团消失,而大量的Ta/NbO双键以Ta/NbO3-结构基团的形式存在,即熔体中存在的是Ta/NbO3-生长基元. |
其他摘要 | The high temperature Raman spectra of KTN crystal and melt were studied.The structures of KTN crystal and melt were analyzed.The rule of structure change of KTN crystal with increasing temperature was analyzed.The results show that the peaks of spectra move to the lower wavelength and broaden by different degrees.The intensities of spectra peaks decrease,too.Raman peaks at 538,585,835,868 and 875cm -1 were analyzed in detail.Phase transition from tetragonal to cubic was observed and explained.In high temperalure KTN melt,the Ta/NbO_6 octahedron entities disappeared.Meanwhile,there were many Ta/Nb O double bonds in the Ta/NbO_3- entities.It showed that there were Ta/NbO3- growth unities in KTN melts. |
关键词 | 高温拉曼光谱 熔体 KTN晶体 |
收录类别 | CSCD |
语种 | 中文 |
CSCD记录号 | CSCD:3488162 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/60919 |
专题 | 中国科学院合肥物质科学研究院 |
推荐引用方式 GB/T 7714 | . KTN晶体及其熔体结构的高温拉曼光谱研究[J]. 物理学报,2009,000. |
APA | (2009).KTN晶体及其熔体结构的高温拉曼光谱研究.物理学报,000. |
MLA | "KTN晶体及其熔体结构的高温拉曼光谱研究".物理学报 000(2009). |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
百度学术 |
百度学术中相似的文章 |
必应学术 |
必应学术中相似的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论