Synthesis and Characterization of Oxide Dispersion Strengthened Ferritic Steel via a Sol-Gel Route | |
其他题名 | Synthesis and Characterization of Oxide Dispersion Strengthened Ferritic Steel via a Sol-Gel Route |
2012 | |
发表期刊 | PLASMA SCIENCE & TECHNOLOGY |
ISSN | 1009-0630 |
摘要 | Nanocrystalline oxide dispersion strengthened (ODS) ferritic steel powders with nominal composition of Fe-14Cr-3W-0.3Ti-0.4Y(2)O(3) are synthesized using sol-gel method and hydrogen reduction. At low reduction temperature the impurity phase of CrO is detected. At higher reduction temperature the impurity phase is Cr2O3 which eventually disappears with increasing reduction time. A pure ODS ferritic steel phase is obtained after reducing the sol-gel resultant products at 1200 degrees C for 3 h. The HRTEM and EDS mapping indicate that the Y2O3 particles with a size of about 15 nm are homogenously dispersed in the alloy matrix. The bulk ODS ferritic steel samples prepared from such powders exhibit good mechanical performance with an ultimate tensile stress of 960 MPa. |
其他摘要 | Nanocrystalline oxide dispersion strengthened (ODS) ferritic steel powders with nominal composition of Fe-14Cr-3W-0.3Ti-0.4Y_2O_3 are synthesized using sol-gel method and hydrogen reduction. At low reduction temperature the impurity phase of CrO is detected. At higher reduction temperature the impurity phase is Cr_2O_3 which eventually disappears with increasing reduction time. A pure ODS ferritic steel phase is obtained after reducing the sol-gel resultant products at 1200°C for 3 h. The HRTEM and EDS mapping indicate that the Y_2O_3 particles with a size of about 15 nm are homogenously dispersed in the alloy matrix. The bulk ODS ferritic steel samples prepared from such powders exhibit good mechanical performance with an ultimate tensile stress of 960 MPa. |
关键词 | ALLOYS POROSITY IRRADIATION ODS ferritic steel sol-gel hydrogen reduction |
收录类别 | CSCD |
语种 | 英语 |
资助项目 | [Innovation Program] ; [Strategic Priority Research Program of Chinese Academy of Sciences] ; [National Magnetic Confinement] ; [Fusion Program] ; [National Natural Science Foundation of China] |
WOS记录号 | WOS:000307123300021 |
CSCD记录号 | CSCD:4589206 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/63655 |
专题 | 中国科学院合肥物质科学研究院 |
推荐引用方式 GB/T 7714 | . Synthesis and Characterization of Oxide Dispersion Strengthened Ferritic Steel via a Sol-Gel Route[J]. PLASMA SCIENCE & TECHNOLOGY,2012,14. |
APA | (2012).Synthesis and Characterization of Oxide Dispersion Strengthened Ferritic Steel via a Sol-Gel Route.PLASMA SCIENCE & TECHNOLOGY,14. |
MLA | "Synthesis and Characterization of Oxide Dispersion Strengthened Ferritic Steel via a Sol-Gel Route".PLASMA SCIENCE & TECHNOLOGY 14(2012). |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
百度学术 |
百度学术中相似的文章 |
必应学术 |
必应学术中相似的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论