铅铋合金中Bi/Bi2O3型氧传感器准确性及稳定性测试研究 | |
其他题名 | Accuracy and Stability Test Study of Bi/Bi2 O3 Oxygen Sensor in Lead-bismuth Eutectic |
2015 | |
发表期刊 | 原子能科学技术 |
ISSN | 1000-6931 |
摘要 | 液态铅铋合金(LBE)中溶解氧浓度的精确测量是实现LBE中氧浓度控制的前提。本文用一自主研制的Bi/Bi2O3型氧传感器来测量LBE氧浓度,在静态氧饱和的LBE中分别进行了准确性及稳定性测试。准确性测试结果表明,在340-480℃范围内氧传感器电动势实验曲线随温度的变化与理论曲线一致,电动势绝对误差最大为-2.6 mV;稳定性测试结果表明,在450℃、50h内电动势绝对误差为-1.4mV,波动为4mV。 |
其他摘要 | Accurate measurement of the concentration of dissolved oxygen in liquid lead‐bismuth eutectic (LBE) is the premise to achieve oxygen control .A self‐developed Bi/Bi2 O3 oxygen sensor was used to measure oxygen concentration in LBE .The accuracy and stability tests were carried out in stagnant liquid LBE in the condition of oxygen sat‐uration .The accuracy test results show that the change of experimental electromotive force with temperature is consistent with the theoretical curve in the temperature ranging from 340 ℃ to 480 ℃ .The maximum absolute error of electromotive force is-2.6 mV .The stability test results show that the absolute error of electromotive force is -1.4 mV within 50 hours at the temperature of 450 ℃ and the fluctuation in this test is4mV . |
关键词 | 铅铋合金 氧浓度 氧传感器 电动势 |
收录类别 | CSCD |
语种 | 中文 |
CSCD记录号 | CSCD:5376138 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/63839 |
专题 | 中国科学院合肥物质科学研究院 |
推荐引用方式 GB/T 7714 | . 铅铋合金中Bi/Bi2O3型氧传感器准确性及稳定性测试研究[J]. 原子能科学技术,2015,049. |
APA | (2015).铅铋合金中Bi/Bi2O3型氧传感器准确性及稳定性测试研究.原子能科学技术,049. |
MLA | "铅铋合金中Bi/Bi2O3型氧传感器准确性及稳定性测试研究".原子能科学技术 049(2015). |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
百度学术 |
百度学术中相似的文章 |
必应学术 |
必应学术中相似的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论