| 钨基面对等离子体材料的制备和性能 | |
| 其他题名 | Fabrication of Tungsten as Plasma Facing Material |
| 2019 | |
| 发表期刊 | 材料科学与工程学报
 |
| ISSN | 1673-2812 |
| 摘要 | 利用等离子体喷涂技术和弥散增强粉末冶金方法制备钨基面对等离子体材料,并对其基本物理属性进行了分析,包括气孔率及其分布、硬度、抗弯强度、结合强度。同时,利用电子束实验装置对钨基复合材料高热负荷性能进行了研究。研究发现,VPS-W涂层能够承受10MW/m^2、100s的热负荷沉积,涂层开裂、分层是其失效原因;TiC和La2O3弥散相增强了钨基复合材料性能,在表面温度控制在1500℃以下可作为面对等离子体材料。 |
| 其他摘要 | Tungsten plasma facing materials(PFM)were fabricated by means of plasma spraying technology and powder metallurgy,respectively.And the main characteristics including porosity and pore size distribution,Vickers hardness,flexural strength,bonding strength between W coating and the substrate,of the tungsten PFM were tested..The performance of the PS-W coating under high heat loading was investigated using the electron beam facility with the water cooling.The results indicate that VPS-W coating can withstanding the heat load of 10 MW/m^2 for 100 s exhibiting the transfer-heat capability better than the APS-W coating.The failure behavior is due to the macro-cracks and delamination.Both of TiC and La2O3 particles can effectively improve the heat performance,the suitable PFM at temperature less than 1500℃for the coating surface. |
| 关键词 | 钨基复合材料 面对等离子体材料 热负荷性能 |
| 收录类别 | CSCD |
| 语种 | 中文 |
| CSCD记录号 | CSCD:6698412 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/64217 |
| 专题 | 中国科学院合肥物质科学研究院 |
| 推荐引用方式 GB/T 7714 | . 钨基面对等离子体材料的制备和性能[J]. 材料科学与工程学报,2019,037. |
| APA | (2019).钨基面对等离子体材料的制备和性能.材料科学与工程学报,037. |
| MLA | "钨基面对等离子体材料的制备和性能".材料科学与工程学报 037(2019). |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 推荐该条目 |
| 保存到收藏夹 |
| 查看访问统计 |
| 导出为Endnote文件 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论