| 空心微珠表面化学沉积Co—P合金研究 | |
| 其他题名 | Electroless plating Co-P alloy on the surface of fly ash cenospheres |
| 2008-01-01 | |
| 发表期刊 | 功能材料
 |
| ISSN | 1001-9731 |
| 摘要 | 利用化学镀工艺在粉煤灰空心微珠表面均匀、完整地包覆磁性Co—P合金层，成功制备出新型轻质的复合导电粉体。使用XRD、EDS、SEM和镶嵌金相的方法对样品进行形貌观察和分析表征，并讨论了镀液温度、pH值和稳定剂浓度对沉积效率的影响。结果表明，空心微珠经过敏化-活化的表面预处理后，利用化学镀方法可以得到均匀、包覆完整的Co-P合金层，并且出现了新的晶化相α-Co单质。T=90℃、pH=10．2和加入适量的硫脲是使反应良好进行的最佳工艺参数。 |
| 其他摘要 | A new kind of composite electric powder can be prepared by electroless plating Co-P alloy on fly ash cenospheres. XRD, EDS, SEM and Metallic microgragh analytical methods are utilized to show the properties and microstructure of the cenospheres coated with Co-P films. The influence of plating temperature, pH value and stabilize agent content on deposition rate are respectively discussed. The results indicate that uniform and high quality Co-P film can be obtained by electroless plating after sensitization and activation. A new crystalline phase of α-Co is appeared on the plating films. Adjusting the plating temperature at 90℃, pH value at 10.2 and adding proper thiourea could enable the reaction well. |
| 关键词 | 空心微珠 化学沉积 Co—P 预处理 |
| 收录类别 | CSCD |
| 语种 | 中文 |
| CSCD记录号 | CSCD:3459165 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/65483 |
| 专题 | 中国科学院合肥物质科学研究院 |
| 推荐引用方式 GB/T 7714 | . 空心微珠表面化学沉积Co—P合金研究[J]. 功能材料,2008,039. |
| APA | (2008).空心微珠表面化学沉积Co—P合金研究.功能材料,039. |
| MLA | "空心微珠表面化学沉积Co—P合金研究".功能材料 039(2008). |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 推荐该条目 |
| 保存到收藏夹 |
| 查看访问统计 |
| 导出为Endnote文件 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论