| ITER校正场线圈接头去镍及表面后处理工艺研究 | |
| 其他题名 | Nickel removal and post surface treatment for ITER CC joint |
田泽均1 ; 吴维越1; 王琳1; 刘丽平1
| |
| 2014 | |
| 发表期刊 | 核聚变与等离子体物理
 |
| ISSN | 0254-6086 |
| 摘要 | 分别采用机械打磨去镍加热镀锡工艺和反电镀去镍加电刷镀银工艺制作一对接头，然后对接头进行低温直流测试，测得前者的直流电阻为1.98nΩ，后者的直流电阻为1.53nΩ。对比分析可知，反电镀去镍和电镀银工艺更有效、更简单。这些工艺研究对ITER校正场线圈超导接头的制作具有重要指导意义。 |
| 其他摘要 | Two joints were manufactured. One was manufactured using mechanical grinding nickel removal method and hot tinning technique. Another was manufactured by anti-plating removing nickel method and brush silver plating technique. The measured DC resistances of the two joints are 1.98nΩand 1.53nΩ respectively. By comparison, anti-plating nickel removing and brush silver plating technique is more effective and easier to processing. All the technique researches are very useful for the fabrication of CC joints. |
| 关键词 | 校正场线圈 超导接头 去镍 电刷镀银 热镀锡 |
| 收录类别 | CSCD |
| 语种 | 中文 |
| CSCD记录号 | CSCD:5092354 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/95304 |
| 专题 | 中国科学院合肥物质科学研究院 |
| 作者单位 | 1.中国科学院等离子体物理研究所 2.中国科学院等离子体物理研究所 3.中国科学院等离子体物理研究所 4.中国科学院等离子体物理研究所 |
| 推荐引用方式 GB/T 7714 | 田泽均,吴维越,王琳,等. ITER校正场线圈接头去镍及表面后处理工艺研究[J]. 核聚变与等离子体物理,2014,034. |
| APA | 田泽均,吴维越,王琳,&刘丽平.(2014).ITER校正场线圈接头去镍及表面后处理工艺研究.核聚变与等离子体物理,034. |
| MLA | 田泽均,et al."ITER校正场线圈接头去镍及表面后处理工艺研究".核聚变与等离子体物理 034(2014). |
| 条目包含的文件 | 条目无相关文件。 | |||||
| 个性服务 |
| 推荐该条目 |
| 保存到收藏夹 |
| 查看访问统计 |
| 导出为Endnote文件 |
| 谷歌学术 |
| 谷歌学术中相似的文章 |
| [田泽均]的文章 |
| [吴维越]的文章 |
| [王琳]的文章 |
| 百度学术 |
| 百度学术中相似的文章 |
| [田泽均]的文章 |
| [吴维越]的文章 |
| [王琳]的文章 |
| 必应学术 |
| 必应学术中相似的文章 |
| [田泽均]的文章 |
| [吴维越]的文章 |
| [王琳]的文章 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论