用La2MoWO9作固体电解质的极限电流型氧传感器 | |
其他题名 | Limiting current type oxygen sensors with La/MoW09 as solid electrolyte |
李丹1; 李相虎1; 方前锋2 | |
2009 | |
发表期刊 | 电子元件与材料 |
ISSN | 1001-2028 |
摘要 | 采用固相反应法,制备了氧离子导体La2MoWO9和混合导体La0.6Sr0.4Fe0.8Co0.2O3,并分别作为基体材料,制成了极限电流型氧传感器。利用两端子法,对氧传感器在500℃时不同氧分压下(PO2为(0~2.12)×10^4Pa)电流与电压的关系进行了测量。结果表明:用La2MoWO9作为氧传感器的固体电解质材料是可行的,即可以得到极限电流平台(PO2为1.70×10^4Pa,1为1.5mA),且极限电流与氧分压戍线性关系。 |
其他摘要 | The oxygen ion conductor La2MoWO9 and mixed conductor La0.6Sr0.4Fe0.8Co0.2O3 were prepared through solid phase reaction method. The limiting current type oxygen sensor was fabricated using them respectively as matrix materials. The relationship between the current and the voltage at different oxygen partial pressure (PO2 = (0-2.12)× 10^4 Pa) was measured at 500 ℃ using the standard two-probe method. The results indicate: it is feasible that the oxygen ion conductor La2MoWO9 is used as solid electrolytes of the limiting current oxygen sensors, that is, the limiting current (PO2= 1.70×10^4pa, I = 1.5 mA) can be achieved, and the relationship between the limiting current and the oxygen partial pressure is linear. |
关键词 | 氧传感器 固体电解质 极限电流 氧分压 |
收录类别 | CSCD |
语种 | 中文 |
CSCD记录号 | CSCD:3536794 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://ir.hfcas.ac.cn:8080/handle/334002/95810 |
专题 | 中国科学院合肥物质科学研究院 |
作者单位 | 1.武汉工业学院,数理科学系 2.武汉工业学院,数理科学系 3.中国科学院固体物理研究所 |
推荐引用方式 GB/T 7714 | 李丹,李相虎,方前锋. 用La2MoWO9作固体电解质的极限电流型氧传感器[J]. 电子元件与材料,2009,028. |
APA | 李丹,李相虎,&方前锋.(2009).用La2MoWO9作固体电解质的极限电流型氧传感器.电子元件与材料,028. |
MLA | 李丹,et al."用La2MoWO9作固体电解质的极限电流型氧传感器".电子元件与材料 028(2009). |
条目包含的文件 | 条目无相关文件。 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
谷歌学术 |
谷歌学术中相似的文章 |
[李丹]的文章 |
[李相虎]的文章 |
[方前锋]的文章 |
百度学术 |
百度学术中相似的文章 |
[李丹]的文章 |
[李相虎]的文章 |
[方前锋]的文章 |
必应学术 |
必应学术中相似的文章 |
[李丹]的文章 |
[李相虎]的文章 |
[方前锋]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论