等离子体熔融生活垃圾焚烧飞灰中试试验

HFCAS OpenIR

	等离子体熔融生活垃圾焚烧飞灰中试试验
其他题名	Pilot Scale Study on Plasma Vitrification of Municipal Waste Incinerator Fly Ash
	黄文有 1; 孟月东2 ; 陈明周 3; 陆杰 3; 吕永红 3
	2016
发表期刊	环境工程技术学报
ISSN	1674-991X
摘要	等离子体熔融飞灰是安全处置飞灰的方法之一。为了获取具有工程应用价值的数据,采用中试规模的等离子体炉在连续进料、出料状态下大批量地熔融飞灰,研究了熔渣、二次飞灰和尾气等产物的特性,测算熔融处理单位质量飞灰的能耗。结果表明：得到的水淬熔渣和自然冷却熔渣的密度分别为3.01和2.90 g/cm^3;重金属浸出毒性远低于GB 5085.3—2007《危险废物鉴别标准浸出毒性鉴别》的标准限值;所采用的等离子体装置在处理280 kg飞灰的连续试验中,飞灰处置能耗为1.12k W·h/kg;二次飞灰的产率为7.1%,其主要成分为NaCl和KCl。
其他摘要	The plasma vitrification is one of the methods of detoxification and disposal of municipal waste incinerator（ MSWI） fly ash. To obtain key data for engineering application,MSWI fly ash was melted with a pilot scale plasma furnace at the conditions of continuous feeding and discharging. The properties of slag,secondary fly ash and off-gas were analyzed,and the energy consumption was calculated. According to the test,the densities of slag quenched by water and air were 3. 01 and 2. 90 g/cm^3,respectively. The leaching test results of heavy metals from the two kinds of slags were all below the limits in Identification standards for hazardous wastes-Identification for extraction toxicity（ GB 5085. 3-2007）. During the pilot scale test,about 280 kg fly ash was melted,and energy consumption of fly ash melting was 1. 12 k W·h/kg. The production ratio of secondary fly ash was 7. 1%,with Na Cl and KCl as its major components.
关键词	生活垃圾焚烧飞灰等离子体熔融无害化重金属
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:5814948
引用统计
文献类型	期刊论文
条目标识符	http://ir.hfcas.ac.cn:8080/handle/334002/96688
专题	中国科学院合肥物质科学研究院
作者单位	1.华南理工大学电子与信息学院 2.中国科学院等离子体物理研究所 3.中广核研究院有限公司 4.中广核研究院有限公司 5.中广核研究院有限公司
推荐引用方式 GB/T 7714	黄文有,孟月东,陈明周,等. 等离子体熔融生活垃圾焚烧飞灰中试试验[J]. 环境工程技术学报,2016,006.
APA	黄文有,孟月东,陈明周,陆杰,&吕永红.(2016).等离子体熔融生活垃圾焚烧飞灰中试试验.环境工程技术学报,006.
MLA	黄文有,et al."等离子体熔融生活垃圾焚烧飞灰中试试验".环境工程技术学报 006(2016).