Sr2FeMoO6薄膜激光感生热电势效应的研究

HFCAS OpenIR

	Sr2FeMoO6薄膜激光感生热电势效应的研究
其他题名	Laser-induced thermoelectric voltage effect of Sr2FeMoO6 film
	陶汝华1 ; 张玉亮 1; 董伟伟 1; 邓赞红1 ; 王波 1; 方晓东1
	2010
发表期刊	量子电子学报
ISSN	1007-5461
摘要	采用脉冲激光沉积法在倾斜SrTO3（100）衬底上制备出高质量的Sr2FeMoO6薄膜，观察到薄膜在可见、红外波段的脉冲激光照射下具有很大的激光感生热电势效应（LITV）。研究表明，用1064nm和532nm波长的脉冲激光从薄膜表面垂直照射时，薄膜表面产生的最大峰值电压分别为0．9V和0．8V，并且LITV信号与激光能量成良好的线性关系，可用以制造高灵敏度的激光功率计／能量计。当激光从SrT03衬底方向照射时，LITV极性发生变化。上述现象用各项异性Seebeck效应给予了解释。
其他摘要	Sr2FeMoO6 film was grown on vicinal-cut SrTiO3 （100） substrate by pulsed laser deposition method. The laser-induced thermoelectric voltage （LITV） was observed when the film was irradiated by visible and infrared pulsed laser. It was found that the maximal peak voltages were 0.9 V and 0.8 V when the film was irradiated by the laser of 1064 nm and 532 nm wavelength, respectively. The intensity of the LITV signals changed linearly with the pulse energy, which can be used as laser power/energy meters with high sensitivity. It was also found the signal polarity was reversed when the sample was irradiated through the substrate rather than at the air/film interface. Anisotropy Seebeck effect is proposed to cause the lateral voltages.
关键词	薄膜激光感生热电势脉冲激光沉积 Sr2FeMoO6 Seebeck效应
收录类别	CSCD
语种	中文
CSCD记录号	CSCD:3944893
引用统计
文献类型	期刊论文
条目标识符	http://ir.hfcas.ac.cn:8080/handle/334002/99619
专题	中国科学院合肥物质科学研究院
作者单位	1.中国科学院安徽光学精密机械研究所 2.中国科学院安徽光学精密机械研究所 3.中国科学院安徽光学精密机械研究所 4.中国科学院安徽光学精密机械研究所 5.中国科学院固体物理研究所 6.中国科学院安徽光学精密机械研究所
推荐引用方式 GB/T 7714	陶汝华,张玉亮,董伟伟,等. Sr2FeMoO6薄膜激光感生热电势效应的研究[J]. 量子电子学报,2010,027.
APA	陶汝华,张玉亮,董伟伟,邓赞红,王波,&方晓东.(2010).Sr2FeMoO6薄膜激光感生热电势效应的研究.量子电子学报,027.
MLA	陶汝华,et al."Sr2FeMoO6薄膜激光感生热电势效应的研究".量子电子学报 027(2010).